KTA Crystal
• High homogeneity, excellent internal quality
• Top quality of surface polishing
• Large block for various size (e.g. 10x10x30mm, 5x5x35mm)
• Large nonlinear coefficient, high conversion efficiency
• Broad transparency range, large temperature matching width
• AR coatings for wave range from visual light to 3300 nm
• Very competitive price, quick delivery
KTA (Potassium Titanyle Arsenate, KTiOAsO4 ) is a nonlinear optical crystal similar to KTP in which atom P is replaced by As. It has good non-linear optical and electro-optical properties, e.g. significantly reduced absorption in band range of 2.0-5.0 µm, broad angular and temperature bandwidth, low dielectric constants.
Compared with KTP, the main advantages of KTA include: higher second-order nonlinear coefficient, longer IR cut-off wavelength, and less absorption at 3.5 µm. KTA also has lower ionic conductivity than that of KTP, which results in a higher laser induced damage threshold.
KTA is very popularly used for Optical Parametric Oscillation (OPO) application which gives high energy conversion efficiency (above 50%) of tunable laser radiation in solid lasers.
WISOPTIC Standard Specifications* - KTA
Dimension Tolerance | ± 0.1 mm |
Cutting Angle Tolerance | < ± 0.25° |
Flatness | < λ/8 @ 632.8 nm |
Surface Quality | < 10/5 [S/D] |
Parallelism | < 20” |
Perpendicularity | ≤ 5' |
Chamfer | ≤ 0.2mm @ 45° |
Transmitted Wavefront Distortion | < λ/8 @ 632.8 nm |
Clear Aperture | > 90% central area |
Coating | AR@1064nm(R<0.2%) & 1533nm(R<0.5%) & 3475nm(R<9%) |
Laser Damage Threshold | 500 MW/cm2 for 1064nm, 10ns, 10Hz (AR-coated) |
* Products with special requirement upon request. | |